PE coated ACP Consisted by two aluminium sheet sandwiching the core of polyethyl
Details
PE coated ACP Consisted by two aluminium sheet sandwiching the core of polyethylene, front side stove-lacquered with a high quality polyester lacquering system, with protective film, reverse side primer coating.
Paint Coating | Specification | Standard | Other (Double PE coating) |
Interior use:
PE (Polyester) | Surface: | Matt & Glossy | |
Coating thickness | 14μm ~ 20μm | 20~25μm | |
Warranty | 6-8 years; | 8~10 Years | |
Panel Thickness | 2mm ~ 7mm, Standard: 3mm, 4mm | ||
ALu Thickness. | 0.02mm~0.5mm, Standard: 0.06mm, 0.1mm, 0.2mm | ||
Width | 1220/1250/1500 | 915,1650,2000... | |
Length | 2440/3000/5000 | 2000~6000mm... | |
Core | PE, LDPE, FR | ||
Colors: | ≧100colors | Others as request | |
Usage: | Indoor (alu skin≦0.2mm) ; Outdoor (Alu skin ≧0.2mm) | ||
Note: | Mirror color, Aluminium Skin thickness ≥0.18mm | ||
PE ACP Feature and advantages
- Outstanding color and glossy retention
- Superior impact and peel strength
- Excellent surface flatness and smoothness
- Lightweight, Excellent Printable surface
- Various colors and easy to install and maintain
Application:
- Signboard usage and advertisement boards
- Building interior wall decoration
- Decoration and renovation the wall of old buildings
- Decoration of shop door, interior wall, ceiling, bathroom, kitchen and balcony, tunnels
Technical data of polyester aluminium composite panel
Aluminium sheet thickness(mm) | 0.04~0.5mm |
Panel thickness tolerance(mm) | ± 0.2 |
Panel width tolerance(mm) | ± 2 |
Panel length tolerance(mm) | ± 3 |
Panel diagonal tolerance(mm) | ± 5 |
Aluminium sheet thickness tolerance(mm) | ± 0.02 |
Paint thickness(Micron) | 12.5μm ~ 25μm |
Paint pencil hardness | > HB |
Paint toughness | 3T |
Impact strength (kg.cm) | 50 |
Temperature resistance | -50℃ to + 90℃ |
Peel strength(180°) | > 5 Newton/mm |
Boiling water resistance | 2 hours without change |
Acid resistance | Immersed surface in 2% HCI for 24 hours, without change |
Alkali resistance | Immersed surface in 2% Ca(OH)2 for 24 hours, without change |
Solvent resistance | 100 times with Dimethylbenzene without change |
Cleaning resistance | Over 100 times without change |
Expansion coefficient(100°K temperature difference) | 2.4 mm/m |